None Metallization 95 Aluminum Oxide Ceramic Structural Parts For HVDC Relay
Product Details:
Place of Origin: | China |
Brand Name: | CMC |
Certification: | IATF16949, ISO9001, ISO14001 |
Model Number: | NE120 |
Payment & Shipping Terms:
Minimum Order Quantity: | 2000 pieces |
---|---|
Price: | USD 1.0~2.50/piece |
Packaging Details: | package adopted plastic film, plastic bag and carton |
Delivery Time: | 20 work days |
Payment Terms: | T/T, Western Union, D/P, D/A, MoneyGram, MoneyGram |
Supply Ability: | 60,000 pieces per month |
Detail Information |
|||
Material: | 95percent Aluminum Oxide | Color: | White, Pink |
---|---|---|---|
Unit: | Piece | Application: | Relay Of EV Cars |
Density: | 3.7g/cm3 | ||
High Light: | None Metallization Structural Parts,95 Aluminum Oxide Ceramic Structural Parts,95 Aluminum Oxide Ceramic Structural Components |
Product Description
None metallization Aluminum Oxide Ceramic Structural Parts for HVDC Relay
1. Description:
The caramic component is none metallization on surface . It is applying to HVDC Relay of EV Cars ,it is made of 95% aluminum oxide.
2. Customized Service
If you need to custom products , Please contact us .Meicheng Co established its mould factory , and we open moulds for customers according to your drawings.
3. Parameters Table:
Product Parameters | ||
Physical Property | Material | 95% Alumina |
Production Process | Dry Pressing | |
Product Dimension | Per customers' drawing | |
Density (g/cm3) | 3.70-3.75g/cm3 | |
Water Absorption | 0% | |
Mechanical Performance | Flexural Strength (Mpa) | 310Mpa |
Modulus of Elasticity (Gpa) | 310Gpa | |
Hardness (Gpa) | 12.9Gpa | |
Poisson Ratio | 0.23 | |
Thermal Character | Linear Thermal Expansion Coefficient | 7.2 |
Heat Conductivity (W/mk) | 23 | |
Electrical Property | Dielectric Constant | 9.2 |
Dielectric Loss Tangent (x10-4) | 8 | |
Insulation Strength (x106V/M) | 15 | |
Metalized Ceramic Performance | Air Tightness (Pa·m3/s) | ≤10-8 |
Bulk Resistivity (Ω·cm) | ≥1010 (20°C), ≥106 (300°C) | |
Bonding Strength (Mpa) | ≥120Mpa | |
Metallization Thickness (μm) | ≥20μm |